Non-xenoestrogenic stabilizers for organic materials

ABSTRACT

A non-xenoestrogenic phosphorus-containing stabilizer for organic materials is disclosed wherein the stabilizer is selected from the group consisting of phosphorus-containing compounds of the structures  
                 
 
     wherein y in an integer of from  6  to  20 , and  
                 
 
     where Z is a linking group, m is  0  or  1 , n is an integer of at least  2 , the asterisks are independently selected terminal groups, R 1 , R 2 , R 3 , R 4 , R 5 , R 6 , R 7 , and R 8  are independently selected from the group consisting of hydrogen, alkyl groups, aralkyl groups, or halogen groups and Q is selected from the group consisting of  
                 
 
     where R 11  is alkyl or aralkyl, and

BACKGROUND OF THE INVENTION

[0001] 1. Field of the Invention

[0002] The present invention relates to stabilizers for polymers andother organic materials. More particularly, the present inventionrelates to stabilizers for polymers or other organic materials that arephosphorus-containing molecules or oligomers that do not act asxenoestrogens.

[0003] 2. Description of Related Art

[0004] Phosphorus-containing antioxidants, such as, phosphites, havebeen used as stabilizers in organic materials, such as, rubber,plastics, oils, and the like. The fourth edition of “Plastic Additives”by Gachter and Muller discusses in great detail the stabilization ofplastics and polymers by commercialized phosphites, such as,tris(nonylphenyl)phosphite (TNPP) andtris(2,4-di-t-butylphenyl)phosphite. TNPP is the primary low cost liquidphosphite stabilizer used in the plastics and rubber industry. Recently,however, plastic and rubber manufacturers have been reluctant to utilizeTNPP in their formulations owing to concerns that TNPP may be axenoestrogen (foreign estrogen). Many of these concerns were raisedrecently in Colburn, T. et al., Our Stolen Future, Dutton (1996) andrelated articles. In this regard, xenoestrogens are suspected of beinghormonally active in developing organisms.

[0005] Non-polymeric phosphite compounds are disclosed in U.S. Pat. No.5,290,747 as primary catalysts for the formation of Nylon 6. The genericstructures of these disclosed phosphites are represented by genericstructure I (where n>5).

[0006] With regard to non-polymeric phosphite stabilizers, two generalclasses of phosphites known in the prior art can be represented bystructures II and III.

[0007] wherein R is H or CH₃ and X is oxygen, sulfur, nitrogen, and thelike. Included in generic structure II is commercially availableIrgaphos 38 (where R=CH₃ and X=H) described in European PatentEP-511156A2. The authors describe the phosphites listed in this patentas stabilizers for organic materials. All the stabilizers listed in EP511156 have structures where R is represented as a methyl group. Much ofthe variation of the group X includes functionalized heteroatoms, suchas, nitrogen, sulfur, oxygen, or functional groups such as cyano,trifluoromethyl, hindered amines, etc. The authors also describestructures wherein R=CH₃ and X is an alkyl or aralkyl group.

[0008] Japanese Patent 54163938 describes the improved thermal stabilityof PVC and ABS polymers containing compounds of structure II where R=Hand X is an ethylene glycol.

[0009] Japanese Patent 55000747 describes a similar composition whereinR=CH₃.

[0010] German patent DE2709528 describes a stabilizer for plastics, suchas, polypropylene, where R=H and X contains a second phosphite in aspiral arrangement.

[0011] British patent GB1180398 describes phosphites (where R=H and theentire group attached to X and including X is a tert-butyl group) usedas thermal stabilizers for SBR or ABS rubber.

[0012] German patent DE4202276 describes a compound related to Irgaphos38 (where R=H and X=H) that is used as a stabilizer for polyolefins.

[0013] Japanese Patent JP03025437 describes a butyl sulfone derivative(where R=H and X=SO₂-butyl) used in silver halide color photographicmaterials to prevent fading of color images.

[0014] Japanese patent JP59004629 describes a phosphite linked toanother phosphite structure through an ether linkage (R=H and X=O). Thisphosphite is used as a photochemical and thermal stabilizer for polymercompounds.

[0015] German patent DE19520337 describes phosphite compounds (R=H, CH₃and X=O) used to stabilize organic materials, such as, polyolefins,lubricants, etc. against oxidative, thermal or photochemicaldegradation.

[0016] A second general class of non-polymeric phosphites is representedby generic structure III. Phosphites within generic structure III arematerials wherein the bis(2,4-di-tert-butylphenol)phosphite groups arejoined symmetrically or non-symmetrically to a linkage group Y.

Structure III

[0017] Japanese patents 58152029, 01038456, and 02225542 describe adiphosphite derivative of III in which the phosphite moieties are linkedtogether via a spiro ether group. These patents describe the use of thisspiro ether linked diphosphite to stabilize polyolefin polymers, suchas, polypropylene, used in radiation sterilizable applications.

[0018] Japanese patents JP54041948, JP54043952, and JP54030241 describediphosphite stabilizers for polymers, such as, polypropylene, where thephosphite moieties are linked via either a bis 1,4-methylene substitutedcyclohexane group or a 2,2-dimethylpropyl group. The diphosphitecontaining the 2,2-dimethylpropyl linkage group is also described as achelating ligand of a hydroformylation catalyst in WO9518089 and in theabove-described GB1180398 where this diphosphite is used as a thermalstabilizer for SBR or ABS rubber. Japanese patent JP61113631 describespolyolefin compositions with improved processing stability and heatresistance with the diphosphite containing the 2,2-dimethylpropyllinkage group. In addition, Japanese patent JP61113631 also describesthe use of a different diphosphite with an n-hexyl group as the linkingagent.

[0019] European patent EP-518241 describes a diphosphite with anunsymmetrical ethyl substituted ethylene linkage group useful as aligand for a hydroformylation catalyst.

[0020] Japanese patent JP02097539 describes a substituted diphenol as anantioxidant for polyolefins.

[0021] European patent EP33395 describes heat and light stabilizers forpolymers also based on a substituted diphenol.

SUMMARY OF THE INVENTION

[0022] The present invention is directed to liquid, non-estrogenicphosphites or polymeric phosphites that provide similar or betterstabilization of organic materials than TNPP.

[0023] More particularly, the present invention relates tophosphorus-containing molecules or low molecular weightphosphorus-containing polymers that act as stabilizers of organicmaterials and do not act as xenoestrogens. Generically, the presentinvention is directed to two types of related alkylated phosphitestabilizers: non-polymeric phosphites and polymeric stabilizers.

[0024] The nonestrogenic phosphite stabilizers of the present inventionpreferably include compounds, such as,bis(2,4-di-t-butylphenyl)octylphosphite (Stabilizer A) and the lowmolecular weight phosphorus-containing polymer (i.e.,phosphorus-containing oligomer)poly(4,4′-{2,2′-dimethyl-5,5′-di-t-butylphenylsulfide}octylphosphite)(Stabilizer B). Stabilizers A and B have the following structures:

[0025] In the above formula for Stabilizer B, n is an integer of atleast 2, preferably from 2 to about 6, more preferably from 2 to 4, R₉and R₁₀ are independently selected from the group consisting of hydrogenand alkyl, preferably alkyl of from 1 to 8 carbon atoms, e.g., methyl,ethyl, propyl, butyl, pentyl, hexyl, heptyl, octyl, isomers of theforegoing, and the like. In a preferred embodiment, R₉ and R₁₀ arehydrogen.

[0026] The oligomeric non-xenoestrogenic phosphorus-containing materialsare of the general structure IV:

[0027] where Z is a linking group, m is 0 or 1, n is an integer of atleast 2, the asterisks are independently selected terminal groups, and Qis selected from the group consisting of

[0028] where R₁₁ is alkyl or aralkyl, preferably having from 1 to 20carbon atoms inclusive, more preferably 6 through 20, most preferably 6through 10, in the alkyl moiety and from 6 to 10 carbon atoms in anyaryl moiety attached thereto, and

[0029] These phosphorus-containing oligomers comprise two main portions:a diphenol portion and a phosphorus portion. The diphenol portioncomprises two substituted phenols that are directly linked (when m is 0)or are coupled by common linking groups (Z) for these materials (when mis 1), such as, for example, isopropylidene, hexafluoroisopropylidene,sulfur, sulfone, or oxygen. The phenol portion of the diphenol can alsobe substituted (R₁-R₈) with alkyl groups, aralkyl groups, or halogengroups.

[0030] More particularly, the present invention is directed to anon-xenoestrogenic phosphorus-containing stabilizer for organicmaterials wherein the stabilizer is selected from the group consistingof phosphorus-containing compounds of the structures

[0031] wherein y in an integer of from 6 to 20, and

[0032] where Z is a linking group, m is 0 or 1, n is an integer of atleast 2, the asterisks are independently selected terminal groups, R₁,R₂, R₃, R₄, R₅, R₆, R₇, and R₈ are independently selected from the groupconsisting of hydrogen, alkyl groups, aralkyl groups, or halogen groupsand Q is selected from the group consisting of

[0033] where R₁₁ is alkyl or aralkyl, and

[0034] In another aspect, the present invention is directed to a methodfor stabilizing an organic material comprising adding to said organicmaterial a non-xenoestrogenic, phosphorus-containing stabilizer selectedfrom the group consisting of phosphorus-containing compounds of thestructures

[0035] wherein y is an integer of from 6 to 20, and

[0036] where Z is a linking group, m is 0 or 1, n is an integer of atleast 2, the asterisks are independently selected terminal groups, R₁,R₂, R₃, R₄, R₅, R₆, R₇, and R₈ are independently selected from the groupconsisting of hydrogen, alkyl groups, aralkyl groups, or halogen groupsand Q is selected from the group consisting of

[0037] where R₁₁ is alkyl or aralkyl, preferably having from 1 to 20carbon atoms inclusive, preferably 6 through 20, more preferably, 6through 10, in the alkyl moiety and from 6 to 10 carbon atoms in anyaryl moiety attached thereto, and

[0038] In still another aspect, the present invention is directed to acomposition of matter comprising an oligomer of the structure

[0039] where Z is a linking group, m is 0 or 1, n is an integer of atleast 2, the asterisks are independently selected terminal groups, R₁,R₂, R₃, R₄, R₅, R₆, R₇, and R₈ are independently selected from the groupconsisting of hydrogen, alkyl groups, aralkyl groups, or halogen groupsand Q is selected from the group consisting of

[0040] where R₁₁ is alkyl or aralkyl, and

BRIEF DESCRIPTION OF THE DRAWING

[0041]FIG. 1 is a graph showing dose-dependent responses of four parentchemicals, along with 17β-estradiol, in the yeast estrogen screen.

DESCRIPTION OF THE PREFERRED EMBODIMENTS

[0042] Organic materials, such as, rubber, plastic resins, lubricatingoils, petroleum fuels, waxes, and organic liquids are well known to needprotection from oxidation. Many of these materials depend on secondaryantioxidants, such as, phosphites, to protect the material fromoxidative degradation and discoloration.

[0043] In particular, the plastic resins can be a thermoplasticpolyolefin, such as, polyethylene, polypropylene, polystyrenes,polyvinylhalides, or other thermoplastic resins, including engineeringthermoplastics. Engineering thermoplastics include resins, such as,polyamides, polyesters, polyphenyleneoxides, polyphenylenesulfides,polyacetals, aliphatic polyketone co or terpolymers,poly(ethersulfones), polycarbonates, liquid crystalline polymers,poly(etheretherketones), and poly(arylates).

[0044] Rubbers include highly unsaturated polymers, such as, natural orsynthetic elastomers, for example, cis-polyisoprene, polybutadiene,poly(styrene-butadiene), polychloroprene, polyacrylonitrile, and thelike, as well as elastomers having lesser unsaturation, such as, EPDM,EPR, and butyl or halogenated butyl rubbers.

[0045] Lubricating oils can include lubrication oil, transmission oils,motor oils, and greases. Petroleum fuels and organic liquids can begasoline, diesel fuel, or jet fuel.

[0046] In particular, thermoplastic polyolefins that can beneficially bestabilized against degradation by means of the compounds of the presentinvention include homopolymers derived from mono and di-ethylenicallyunsaturated hydrocarbon monomers having at least three carbon atoms,such as, polypropylene, polyisobutylene, polymethylbutene-1,polymethylpentene-1, polybutene-1, polystyrene (including polymers ofstyrene, such as, impact polystyrene, ABS resin oracrylonitrile/butadiene/styrene copolymer, and SBR), polyisobutylene,and the like; copolymers derived from two or more monomers such asethylene-propylene copolymers having at least a majority of propylene,propylene-butene-1 copolymers, propylene-isobutylene copolymers, andblends of a majority of polypropylene with a minority of polyethylene,propylene, and polybutene-1, and propylene and polyisobutylene.

[0047] The foregoing polyolefin homopolymers, copolymers, and blendsthereof can be combined with minor amounts by weight, i.e., less thanabout 50 weight percent and preferably less than 20 weight percent, ofone or more compatible or compatibilized polymers other than thosementioned, for example, polyvinylhalides, chlorinated polyolefins,polyesters, polyamides, polyacrylates, and the like.

[0048] As stated above, the present invention is directed anon-xenoestrogenic phosphorus-containing stabilizer for organicmaterials wherein the stabilizer is selected from the group consistingof phosphorus-containing compounds of the structures

[0049] wherein y in an integer of from 6 to 20, and

[0050] where Z is a linking group, m is 0 or 1, n is an integer of atleast 2, the asterisks are independently selected terminal groups, R₁,R₂, R₃, R₄, R₅, R6, R₇, and R₈ are independently selected from the groupconsisting of hydrogen, alkyl groups, aralkyl groups, or halogen groupsand Q is selected from the group consisting of

[0051] where R₁₁ is alkyl or aralkyl, preferably having from 1 to 20carbon atoms inclusive, more preferably 6 through 20, most preferably 6through 10, in the alkyl moiety and from 6 to 10 carbon atoms in anyaryl moiety attached thereto, and

[0052] In the above structural formula, the linking group Z ispreferably selected from the group consisting of alkylene, substitutedalkylene, sulfur, sulfone, and oxygen.

[0053] Where Z is alkylene, it is preferably alkylene of from 1 to 20carbon atoms, e.g., methylene, ethylene, propylene, butylene, pentylene,hexylene, heptylene, octylene, nonylene, decylene, undecylene,dodecylene, tridecylene, tetradecylene, pentadecylene, hexadecylene,heptadecylene, octadecylene, nonadecylene, eicosylene, isomers of theforegoing, and the like.

[0054] Where Z is a substituted alkylene, it is preferably an alkyleneof from 1 to 20 carbon atoms as described above having anysubstituent(s) attached thereto that will not adversely affect thestabilizing properties of the compound. Preferably, such substituent(s)will be one or more halogens, e.g., fluoro, chloro, bromo, or iodo.

[0055] The coupler, Q, of the above structural formula is preferablypentaerythritol diphosphite.

[0056] The chain terminating groups of the above formula can be, forexample, hydrogen on the left side of the formula and, on the rightside,

[0057] where R₁₂ and R₁₃ are independently selected from the groupconsisting of hydrogen and alkyl of from 1 to 8 carbon atoms. It ispreferred that both R₁₂ and R₁₃ be hydrogen.

[0058] In the above formula, R₁, R₂, R₃, R₄, R₅, R₆, R₇, and R₈ areindependently selected from the group consisting of hydrogen, alkylgroups, aralkyl groups, or halogen groups. Where any of R₁, R₂, R₃, R₄,R₅, R₆, R₇, and R₈ are alkyl, they are preferably alkyl of from 1 to 20carbon atoms, e.g., methyl, ethyl, propyl, butyl, pentyl, hexyl, heptyl,octyl, nonyl, decyl, undecyl, dodecyl, tridecyl, tetradecyl, pentadecyl,hexadecyl, heptadecyl, octadecyl, nondecyl, eicosyl, and isomers of theforegoing. It is more preferred that where any of R₁, R₂, R₃, R₄, R₅,R₆, R₇, and R₈ are alkyl they are alkyl of from 1 to 8 carbon atoms,most preferred that they are of from 1 to 4 carbon atoms, i.e., methyl,ethyl, propyl, isopropyl, butyl, isobutyl, sec-butyl, or tert-butyl.Where any of R₁, R₂, R₃, R₄, R₅, R₆, R₇, and R₈ are aralkyl, the alkylmoiety is preferably of from 1 to 20 carbon atoms, as described above,and the aryl moiety is preferably of from 6 to 10 carbon atoms, e.g.,phenyl, naphthyl, anthracyl, phenanthryl, and the like, more preferablyphenyl. Such aryl moieties can be further substituted, if desired, withadditional groups that will not adversely affect the stabilizingproperties of the compound. Where any of R₁, R₂, R₃, R₄, R₅, R₆, R₇, andR₈ are halogen, they are preferably fluoro, chloro, bromo, or iodo.

[0059] In the above formulae, y is an integer of from 6 to 20,preferably from 6 to 12, more preferably, from 6 to 10 and x is aninteger of from 1 to 20, preferably 1 to 12, more preferably 1 to 10.

[0060] The amount of the stabilizers of the present inventionincorporated into the foregoing organic materials will, at a minimum, bethat required to impart a significant level of stability againstoxidative degradation. In general, such amounts can vary from about 0.01to about 5.0, and preferably from about 0.05 to 0.5, weight percent,where the organic material is a polyolefin homopolymer, copolymer, orpolyolefin blend. Although amounts of the stabilizer in excess of about5 weight percent can be employed, such amounts may have a deleteriouseffect on the physical and mechanical properties of the polyolefinsubstrate, in which case they should be ordinarily be avoided.

[0061] The procedures employed to incorporate the stabilizers into anorganic material are not critical and, in general, follow any of theknown procedures for incorporating additives in such compositions. Forexample, these stabilizers can be introduced into a polyolefin andhomogeneously distributed throughout the polymer by milling, extrusionblending, or other mechanical working procedure. The stabilizer can beadded to the polyolefin by way of a preconcentrate or in a carriersystem, for example, in a suitable solvent or co-solvent.

[0062] Following common practice, other additives can be introduced intothe organic material prior to, during, and/or following addition of thestabilizer. The additives of this invention can be used in combinationor with other additives typically found in organic materials. Theseadditives can be primary antioxidants, such as, hindered phenols, amineantioxidants, other secondary antioxidants, such as, thioesters, orprocessing agents, metal deactivators, light stabilizers, fillers,antistatic agents, colorants, reinforcements, lubricants, plasticizers,and the like, present in their customary amounts.

[0063] Examples of antioxidants that can be used with the stabilizers ofthe present invention include, but are not limited to,2,6-di-tert.-butyl-4-methylphenol, 2-tert-butyl-4,6-dimethylphenol,2,6-di-tert.-butyl-4-methoxymethylphenol,2,6-dioctadecyl-4-methylphenol, 2,5-di-tert.-butyl-hydroquinone,2,5-di-tert.-amylhydroquinone, 2,6-di-tert.-butyl-hydroquinone,2,5-di-tert.-butyl-4-hydroxy-anisole,3,5-di-tert.-butyl-4-hydroxy-anisole, 3,5-di-tert.-butyl-4-hydroxyphenylstearate, bis-(3,5-di-tert.-butyl-4-hydroxyphenyl) adipate,2,2′-thio-bis-(6-tert.-butyl-4-methylphenol),2,2′-thio-bis-(4-octylphenol),4,4′-thio-bis-(6-tert.-butyl-3-methylphenol),4,4′-thio-bis-(3,6-di-sec.-amylphenol),4,4′-thio-bis-(6-tert.-butyl-2-methylphenol),4,4′-bis-(2,6-dimethyl-4-hydroxyphenyl) disulphide,2,2′-methylene-bis-(6-tert.-butyl-4-methylphenol),2,2′-methylene-bis-(6-tert.-butyl-4-ethylphenol),4,4′-methylene-bis-(6-tert.-butyl-2-methylphenol),4,4′-methylene-bis-(2,6-di-tert.-butylphenol),2,6-di-(3-tert.-butyl-5-methyl-2-hydroxybenzyl)-4-methylphenol,2,2′-methylene-bis-[4-methyl-6(.alpha.-methylcyclohexyl)-phenol],1,1-bis-(3,5-dimethyl-2-hydroxyphenyl)-butane,1,1-bis-(5-tert.-butyl-4-hydroxy-2-methylphenyl)-butane,2,2-bis-(3,5-di-tert.-butyl-4-hydroxyphenyl)-propane,1,1,3-tris-(5-tert.-butyl-4-hydroxy-2-methylphenyl)-butane,2,2-bis-(5-tert.-butyl-4-hydroxy-2-methylphenyl)-4-n-dodecylmercaptobutane,1,1,5,5-tetra-(5-tert.-butyl-4-hydroxy-2-methylphenyl)-pentane, ethyleneglycol bis-(3,3-bis-(3′-tert.-butyl-4′-hydroxyphenyl)-butyrate),octadecyl 4-hydroxy-3,5-dimethylbenzyl mercaptoacetate,tris-(3,5-di-tert.-butyl-4-hydroxybenzyl)amine,bis-(4-tert.-butyl-3-hydroxy-2,6-dimethylbenzyl) dithioterephthalate,dioctadecyl 2,2-bis-(3,5-di-tert.-butyl-2-hydroxybenzyl)-malonates,dioctadecyl 2-(3-tert.-butyl-4-hydroxy-5-methylbenzyl)-malonate,di-dodecylmercapto-ethyl2,2-bis-(3,5-di-tert.-butyl-4-hydroxybenzyl)-malonate,di-(4-(1,1,3,3-tetramethyl)phenyl)2,2-bis-(3,5-di-tert.-butyl-4-hydroxybenzyl)-malonate,1,3,5-tri-(3,5-di-tert.-butyl-4-hydroxybenzyl)-2,4,6-trimethylbenzene,1,4-di-(3,5-di-tert.-butyl-4-hydroxybenzyl)-2,3,5,6-tetramethylbenzene,2,4,6-tri-(3,5-di-tert.-butyl-4-hydroxybenzyl)-phenol,2,4-bis-octylmercapto-6-(3,5-di-tert.-butyl-4-hydroxyanilino)-s-triazine,2-octylmercapto-4,6-bis-(3,5-di-tert.-butyl-4-hydroxyanilino)-s-triazine,2-octylmercapto-4,6-bis-(3,5-di-tert.-butyl-4-hydroxyphenoxy)-s-triazine,2,4,6-tris-(3,5-di-tert.-butyl-4-hydroxyphenoxy)-s-triazine,2,4,6-tris-(3,5-di-tert.-butyl-4-hydroxyphenylethyl)-s-triazine,1,3,5-tris-(3,5-di-tert.-butyl-4-hydroxybenzyl) isocyanurate,1,3,5-tris-(3,5-di-tert.-butyl-4-hydroxyphenyl-propionyl)-hexahydro-s-triazineandN,N-di-(3,5-di-tert.-butyl-4-hydroxyphenyl-propionyl)-hexamethylenediamine,N,N′-(bis-p-(3,5-di-t-butyl-4-hydroxyphenyl)-propionyl)-hydrazine,esters of β-(3,5-di-tert.-butyl-4-hydroxyphenyl)-propionic acid,β-(5-tert.-butyl-4-hydroxy-3-methylphenyl)-propionic acid, or3,5-di-tert.-butyl-4-hydroxyphenylacetic acid with monohydric orpolyhydric alcohols, dimethyl3,5-di-tert.-butyl-4-hydroxybenzyl-phosphonate, diethyl3,5-di-tert.-butyl-4-hydroxybenzyl-phosphonate dioctadecyl3,5-di-tert.-butyl-4-hydroxybenzyl-phosphonate, and dioctadecyl5-tert.-butyl-4-hydroxy-3-methylbenzylphosphonate.

[0064] Examples of further additives that can be used together with thestabilizers of the present invention include, but are not limited to:

[0065] aminoaryl derivatives, e.g. phenyl-1-naphthylamine,phenyl-2-naphthylamine, N,N′-diphenyl-p-phenylenediamine,N,N′-di-2-naphthyl-p-phenylenediamine,N,N′-di-2-naphthyl-p-phenylenediamine,N,N′-di-sec.-butyl-p-phenylenediamine,6-ethoxy-2,2,4-trimethyl-1,2-dihydroquinoline,6-dodecyl-2,2,4-trimethyl-1,2-dihydroquinoline, mono- anddioctyliminodibenzyl, polymerized 2,2,4-trimethyl-1,2-dihydroquinoline,octylated diphenylamine, nonylated diphenylamine,N-phenyl-N′-cyclohexyl-p-phenylenediamine,N-phenyl-N′-isopropyl-p-phenylenediamine,N,N′-di-sect-octyl-p-phenylenediamine,N-phenyl-N′-sec.-octyl-p-phenylenediamine,N,N′-di(1,4-dimethylpenthyl)-p-phenylenediamine,N,N′-dimethyl-N,N-di-(sec.-octyl)-p-phenylenediamine,2,6-dimethyl-4-methoxyaniline, 4-ethoxy-N-sec.-butylaniline,di-phenylamineacetone condensation product, aldol-1-naphthylamine andphenothiazine; UV-absorbers and light-stabilizing agents, such as,2-(2′-hydroxyphenyl)-benzotriazoles,2,4-bis-(2′-hydroxyphenyl)-6-alkyl-s-triazines, 2-hydroxybenzophenones,1,3-bis-(2′-hydroxybenzoyl)-benzenes, esters of optionally substitutedbenzoic acids, e.g. phenylsalicylate, octylphenylsalicylate,dibenzoylresorcin, bis-(4-tert.-butylbenzoyl)-resorcin, benzoylresorcin,3,5-di-tert.-butyl-4-hydroxybenzoic acid-2,4-di-tert.-butylphenyl esteror -octadecyl ester or-2-methyl-4,6-di-tert.-butylester, acrylates, e.g.α-cyano-β,β-diphenylacrylic acid-ethyl ester or -isooctyl ester,α-carbomethoxy-cinnamic acid methyl ester,α-cyano-β-methyl-p-methoxycinnamic acid methyl ester or -butyl ester orN-(β-carbomethoxyvinyl)-2-methyl-indoline, sterically hindered amines,e.g. 4-benzoyl-2,2,6,6-tetramethylpiperidine,4-stearyloxy-2,2,6,6-tetramethylpiperidine,bis-(2,2,6,6-tetramethylpiperidyl)-sebacate or3-n-octyl-7,7,9,9-tetramethyl-1,3,8-tetramethyl-1,3,8-triazaspiro(4,5)decane-2,4-dione,oxalic acid diamides, e.g. 4,4′-di-octyloxy-oxanilide,2,2′-di-octyloxy-5,5′-di-tert.-butyl-oxanolide.2,2′-di-dodecyloxy-5,5′-di-tert.-butyl-oxanilide,2-ethoxy-2′-ethyl-oxanilide, N,N′-bis-(3-dimethylaminopropyl)-oxalamide,2-ethoxy-5-tert.-butyl-2′-ethyl-oxanilide and the mixtures thereof with2-ethoxy-2′-ethyl-5,4′-di-tert.-butyl-oxanilide, or mixtures of ortho-and paramethoxy- as well as of o- and p-ethoxy-disubstituted oxanilides;metal deactivators, e.g., oxanilide, isophthalic acid dihyrazide,sebacic acid-bis-phenylhydrazide, bis-benzylidene-oxalic aciddihydrazide, N,N′-diacetal-adipicaciddihydrazide,N,N′-bis-salicyloyloxalic acid dihydrazide,N,N′-bis-salicyloylhydrazine,N,N′-bis(3,5-di-tert.-butyl-4-hydroxyphenylpropionyl)hydrazine,N-salicyloyl-N′-salicylalhydrazine, 3-salicyloylamino-1,2,4-triazole orN,N′-bis-salicyloyl-thiopropionic acid dihydrazide; basicco-stabilizers, e.g., alkali metal salts and alkaline-earth metal saltsof higher fatty acids, e.g., Ca-stearate, Zn-stearate, Mg-behenate,Na-ricinoleate or K-palmitate; nucleation agents, e.g.,4-tert.-butylbenzoic acid, adipic acid or diphenylacetic acid;phosphites, e.g., triphenyl phosphite, diphenylalkyl phosphites,phenyldialkyl phosphites, tri-(nonylphenyl) phosphite, trilaurylphosphite, trioctadecyl phosphite, 3,9-isodecyloxy-2,4,8,10-tetraoxa3,9-diphospha(5,5)-undecane and tri-(4-hydroxy-3,5-di-tert.butylphenyl)phosphite.

[0066] Other additives that can be incorporated in the stabilizedcompositions are thiosynergists, such as, dilaurylthiodiproprionate ordistearylthiodipropionate, lubricants, such as, stearyl alcohol,fillers, carbon black, asbestos, lanolin, talc, glass fibers, pigments,optical brighteners, fireproofing agents, and antistatic agents.

[0067] The advantages and the important features of the presentinvention will be more apparent from the following examples.

EXAMPLES Example 1 Synthesis of Octylphosphorodichloridite

[0068] Freshly distilled phosphorus trichloride (45.6 g, 0.338 mole) wascharged into a four-necked round bottom flask equipped with a mechanicalstirrer, an addition funnel, a thermometer, and a reflux condenseritself topped with a discharge tube. The discharge tube led to anaqueous sodium hydroxide trap for absorption of hydrogen chloride thatevolves from the reaction. After cooling the reaction vessel to 0° C.with continual purging of dry nitrogen, anhydrous octanol (22 g, 0.168mole) was added dropwise to the reaction mixture. When the addition ofthe octanol was complete, the reaction mixture was allowed to warmgradually up to room temperature and was then poured into a drydistillation flask. The material was distilled with a bath temperatureof 80-85° C. and using a water pump vacuum to remove residual hydrogenchloride and excess phosphorus trichloride. The residue was thenfractionated at 8 mm Hg to yield the product at 113-130° C. in 69%conversion. The phosphorus-31 NMR showed a peak at 176 ppm. Therefractive index at 21.5° C. was 1.4682.

Example 2 Synthesis of Bis(2,4-di-t-butylphenyl)octylphosphiteStabilizer A

[0069] Anhydrous benzene (165 mL), 2,4-di-t-butylphenol (41.2 g) andanhydrous triethylamine (21.0 g, 28.7 mL, 34% excess) was charged into athree necked flask, equipped with a mechanical stirrer, reflux condenserand thermometer. After heating the reaction mixture to 35-40° C., 23.1 gof the octylphosphorodichloridite of Example 1 was added. The reactionwas heated to 80-85° C. and the reaction mixture was stirred for fourhours. The hydrochloride salt of the triethylamine precipitated and wasfiltered off on a hot funnel and washed with hot benzene. Benzene andexcess triethylamine were removed from the filtrate under vacuum. Theresidue was a mobile, turbid, slightly yellowish product that was againfiltered through a hot funnel to remove the small quantity ofprecipitated salt of triethylamine. The now transparent reaction masswas treated under vacuum at a temperature of 80-85° C. and a pressure of8-10 mm Hg for 1.5-2 hours. The small quantity of precipitated salt oftriethylamine was once again filtered off with a funnel leaving atransparent, viscous product of slightly yellowish color. Thephosphorus-31 NMR showed a peak at 124 ppm.

Example 3 Synthesis ofPoly(4,4′-{2,2′-dimethyl-5,5′-di-t-butylphenylsulfide}octylphosphite)Stabilizer B

[0070] To a round bottom flask was added 34.6 g (0.1 mol) ofdiphenyl-(2-ethylhexyl)phosphite, 35.8 g (0.1 mol) of 4,4′-thiobis(3-methyl-6-tert-butylphenol), and a catalytic quantity of metallicsodium (or alcoholate of an alkali metal). The mixture was heated at180° C. under an atmosphere of nitrogen for one hour. The temperaturewas reduced to 90-100° C. and the phenol was removed under vacuum (10mm) over 2.5 hours. When the residual pressure dropped to 1 mm, thereaction mass was subjected to vacuum for two more hours. The residualtransparent glassy resin was then ground into a powder. MP=62° C. Theyield was quantitative. The phosphorus-31 NMR showed a series of peaksfrom 126 to 131 ppm.

[0071] MW_(meas.) (cryoscopic in benzene)=1680, n=3, %P 5.63; %S 5.57.

[0072] MW_(calc.)=1642; %P 5.66; %S 5.84

[0073] Syntheses of all polyphosphites are carried out by thepoly-transesterification reaction of alkyldiphenyl-phosphite ortriphenylphosphite or an appropriate bis-phenol. If the initialbis-phenol does not contain alkyl substituents in the phenolic nucleus,the poly-transesterification reaction proceeds in the absence ofcatalysts.

Example 4 Synthesis ofPoly(4,4′-{isopropylidenediphenol}-octylphosphite) Stabilizer C

[0074] In a round bottom flask, 34.6 g (0.1 mol) ofdiphenyl-(2-ethylhexyl)phosphite, 22.8 g (0.1 mol) of bisphenol-A, and acatalytic quantity of metallic sodium (or alcoholate of an alkali metal)was heated at 180° C. under an atmosphere of nitrogen for one hour. Thetemperature was reduced to 90-100° C. The phenol was then removed undervacuum (10 mm) over 2.5 hours. When the residual pressure dropped to 1mm, the reaction mass was subjected to vacuum for two more hours. Theyield was quantitative. The phosphorus-31 NMR showed a series of peaksfrom 126 to 131 ppm.

Example 5 Synthesis ofPoly(4,4′-{isopropylidenebis[2,6-dibromophenol]}-octylphosphite)Stabilizer D

[0075] In a round bottom flask, 34.6 g (0.1 mol) of diphenyl(2-ethylhexyl) phosphite, 54.4 g (0.1 mol) ofteterabromodiphenylpropane, and a catalytic quantity of metallic sodiumwas heated for 1 hour under vacuum (9 mm) at 120° C. The phenol wasremoved over 6 hours as the temperature gradually was raised up to 190°C. For complete stripping of phenol, the pressure was brought to 1 mm.The residue after stripping of the phenol was ground into a light yellowpowder that melted at 64° C.

[0076] MW_(meas.) (cryoscopic)=1510, %P 3.8.

[0077] MW_(calc.)=1437 (n˜2), %P 4.1.

Example 6 Synthesis ofPoly(4,4′-{2,2′-dimethyl-5,5′-di-t-butylphenylsulfide}-pentaerythrityldiphosphite) Stabilizer E

[0078] A flask containing 13.6 g (0.1 mol) of pentaerythritol and 62.0 g(0.2 mol) of triphenylphosphite was heated under vacuum (8-10 mm Hg) at90-95° C. for one hour to strip off phenol. Gradually the temperaturewas raised to 170° C., and the pressure was reduced to 1 mm Hg. Theremaining residue was diphenylpentaerythrityldiphosphite.

[0079] The diphenylpentaerythrityldiphosphite thus obtained was mixedwith 35.8 g (0.1 mol) 4,4′-thiobis(3-methyl-6-tert-butylphenol). Thethiobisphenol was melted into the diphosphite under a vacuum (8-10 mm)while the phenol was removed. The temperature was gradually raised from100 to 175° C. Any residual phenol was removed at 1 mm Hg. The resultingproduct was transparent and glass-like and was ground into a whitepowder. The phosphorus-31 NMR showed a series of peaks from 85 to 132ppm. T_(m)=69° C.

[0080] MW_(meas.) 1120. (n˜2). %P 11.03; %S 5.06.

[0081] MW_(calc.) 1194; %P 10.76; %S 5.36

Example 7 Xenoestrogenicity Testing

[0082] To determine the relative “endocrine” activity of severalphosphite stabilizers, each was evaluated for biological activity in anin vitro assay developed to assess estrogenicity.

[0083] The assay employs a genetically engineered (recombinant) strainof yeast that generates and releases the enzyme β-galactosidase in thepresence of β-17 estradiol (estrogen) or a xenoestrogen. In the culturemedium, β-galactosidase is broken down to the chromogenic substratechlorophenol red-β-D-galactopyranoside (CPRG). The activity and relativepotency of xenoestrogen is determined spectrophotometrically. Fulldetails of the assay have been discussed previously (Routledge, E. J. etal., Environ. Tox. & Chem. 15(3):241-248 (1996)).

[0084]FIG. 1 shows the relative “estrogenic” activity of severalstructurally related phosphite stabilizers.

Example 8

[0085] Tables 1-12 detail the performance of the Stabilizers A-E inpolyolefins. These compounds show performance as plastic stabilizersthat is comparable to or better than that of TNPP. With regard to MeltFlow Rate (MFR), a good plastic stabilizer will contribute to a lowinitial MFR and then maintain the low MFR. For Hunter b Colorperformance, a good plastic stabilizer will yield low initial color andthen maintain that low color. For Long Term Heat Aging (LTHA) andOxidative Induction Time (OIT), a good stabilizer will have a longerLTHA and OIT value.

[0086] Sample Preparation

[0087] The polyolefin powder (polyethylene or polypropylene) is dryblended with the stabilizer formulation using a typical household mixer.The mixer is run at approximently 60 rpm or a speed which does not causethe material to splash out of the bowl for at least 15 minutes. Themasterbatch is then added to a preheated single screw extruder where theplastic is homogeneously mixed. Extrusion is typically performed at 200°C. for polyethylene and 250° C. for polypropylene. The extruded plasticis cooled into a cold water bath, completely dried, and pelletized. Thecollected polymer pellets are the result of the first pass extrusion andare the starting material for all subsequent test protocols. Theisolated pellets are added to the extruder repeatedly to generate thethird and fifth pass material.

[0088] Melt Flow Rate Analysis

[0089] The melt flow rate was performed using the ASTM 1238-90b testmethod measured at 2.16 Kg/230° C. The melt flow rate was completed oneither an IIRT-M2 or Tinius Olsen extrusion plastometer.

[0090] Color Analysis

[0091] Color analysis was performed on compression molded films orplaques with either a Hunter Lab Ultrascan XE or Datacolour machine.Observations were made with a D65 illuminant and 10° observer.Yellowness Index measurements were made in accord with ASTM D 1925-70and Hunter b Color measurements were calculated using formulas in ASTMD1925-77.

[0092] Long Term Heat Aging

[0093] Heat aging was performed based on methods in ASTM D3045-92 usinga circulating air oven. The oven temperature is typically set at 90° C.for polyethylene and 140° C. for polypropylene. The samples were checkeddaily for degradation based on yellowing, brittleness, or crumbling.

[0094] Oxidative Induction Times

[0095] The antioxidant properties of the novel product in a fullyformulated plastic are determined in the Oxidation Induction Time (OIT)test under ASTM D3895 conditions. The test is performed at 200° C. forpolyethylene and 180° C. for polypropylene. Circular disks are cut from0.25 mm films of the material to be tested and placed in aluminum pansfor use in a Perkin-Elmer DSC-2C differential scanning calorimeter(DSC). The test chamber of the DSC calorimeter is purged with nitrogenduring conditioning to an isocratic temperature at 200° C. (or 180° C.for PP). Conditioning is followed by immediate change to oxygen at aflow rate of 20 cc's per minute to induce thermal oxidative degradation.OIT is the time span in minutes between reaching an isocratictemperature when the oxygen environment is introduced and the time atwhich the DSC detects the onset of oxidation. In the OIT test, a longerOIT value indicates better oxidative stability of the formulation andthe results are the average of at least three tests.

[0096] In the following tables, BHT is 2,6-di-t-butyl-4-methyl phenol(i.e., butylated hydroxy toluene) and Naugard 10 istetrakis{methylene(3,5-di-t-butyl-4-hydroxy-hydrocinnamate)}methane.TABLE 1 Melt Flow Rate Polypropylene with 0.05% Calcium StearateStabilizer (0.2%) Phenolic (0.1%) First Pass Third Pass Fifth Pass NoneNaugard 10 3.5 4.0 4.5 TNPP Naugard 10 3.1 3.3 3.6 B Naugard 10 3.0 3.13.2 E Naugard 10 3.1 3.2 3.4 D Naugard 10 3.6 4.1 4.7

[0097] TABLE 2 Yellowness Index Polypropylene with 0.05% CalciumStearate Stabilizer (0.2%) Phenolic (0.1%) First Pass Third Pass FifthPass None Naugard 10 13 19 26 TNPP Naugard 10 13 18 25 B Naugard 10 1319 24 E Naugard 10 13 19 25 D Naugard 10 13 17 23

[0098] TABLE 3 Polypropylene with 0.05% Calcium Stearate OIT @Stabilizer (0.2%) Phenolic (0.1%) LTHA (days) 180° C. (min) None Naugard10 58  44 TNPP Naugard 10 66 209 B Naugard 10 58 648 E Naugard 10 73 270D Naugard 10 65  44

[0099] TABLE 4 Melt Flow Rate Polypropylene with 0.05% Calcium StearateStabilizer (0.05%) Phenolic (0.05%) First Pass Third Pass Fifth PassNone BHT 5.69 6.46 7.29 TNPP BHT 4.87 5.48 6.32 C BHT 4.54 5.24 5.81

[0100] TABLE 5 Hunter b Color Polypropylene with 0.05% Calcium StearateStabilizer (0.05%) Phenolic (0.05%) First Pass Third Pass Fifth PassNone BHT 1.26 1.57 1.98 TNPP BHT 1.13 1.52 1.88 C BHT 1.06 1.25 1.53

[0101] TABLE 6 Polypropylene with 0.05% Calcium Stearate Stabilizer(0.05%) Phenolic (0.05%) LTHA (days) None Naugard 10 20 TNPP Naugard 1027 C Naugard 10 31

[0102] TABLE 7 Melt Flow Rate Polypropylene with 0.05% Calcium StearateStabilizer (0.2%) Phenolic (0.1%) First Pass Third Pass Fifth Pass NoneBHT 5.45 5.95 6.84 TNPP BHT 4.47 5.02 5.60 A BHT 3.73 4.21 4.67

[0103] TABLE 8 Hunter b Color Polypropylene with 0.05% Calcium StearateStabilizer (0.2%) Phenolic (0.1%) First Pass Third Pass Fifth Pass NoneBHT 1.40 1.84 2.72 TNPP BHT 1.35 1.50 1.77 A BHT 1.37 1.43 1.59

[0104] TABLE 9 Polypropylene with 0.05% Calcium Stearate OIT @Stabilizer (0.2%) Phenolic (0.1%) LTHA (days) 180° C. (min) None Naugard10 36 25 TNPP Naugard 10 50 73 A Naugard 10 42 153 

[0105] TABLE 10 Melt Flow Rate Polyethylene Stabilizer (0.2%) Phenolic(0.1%) First Pass Third Pass Fifth Pass None Naugard 10 1.0245 1.05121.0845 TNPP Naugard 10 1.0293 1.0631 1.0899 A Naugard 10 1.0427 1.05861.0698

[0106] TABLE 11 Hunter b Color Polyethylene Stabilizer (0.2%) Phenolic(0.1%) First Pass Third Pass Fifth Pass None Naugard 10 0.85 2.01 2.58TNPP Naugard 10 −0.41 −0.18 −0.13 A Naugard 10 −0.45 −0.43 −0.30

[0107] TABLE 12 Polyethylene Stabilizer (0.2%) Phenolic (0.1%) OIT @200° C. (min) None Naugard 10 18 TNPP Naugard 10 53 A Naugard 10 122 

[0108] In view of the many changes and modifications that can be madewithout departing from principles underlying the invention, referenceshould be made to the appended claims for an understanding of the scopeof the protection afforded the invention.

What is claimed is:
 1. A non-xenoestrogenic phosphorus-containingstabilizer for organic materials wherein the stabilizer is selected fromthe group consisting of phosphorus-containing compounds of thestructures

wherein y in an integer of from 6 to 20, and

where Z is a linking group, m is 0 or 1, n is an integer of at least 2,the asterisks are independently selected terminal groups, R₁, R₂, R₃,R₄, R₅, R6, R₇, and R₈ are independently selected from the groupconsisting of hydrogen, alkyl groups, aralkyl groups, or halogen groupsand Q is selected from the group consisting of

where R₁₁ is alkyl or aralkyl, and


2. The stabilizer of claim 1 wherein the organic material is selectedfrom the group consisting of rubbers, plastic resins, lubricating oils,petroleum fuels, and waxes.
 3. The stabilizer of claim 1 wherein theorganic material is a plastic resin.
 4. The stabilizer of claim 3wherein the plastic resin is a thermoplastic resin.
 5. The stabilizer ofclaim 4 wherein the thermoplastic resin is a thermoplastic polyolefin oran engineering thermoplastic.
 6. The stabilizer of claim 4 wherein thethermoplastic resin is selected from the group consisting ofpolyethylene, polypropylene, polystyrenes, polyvinylhalides, polyamides,polyesters, polyphenyleneoxides, polyphenylenesulfides, polyacetals,aliphatic polyketone co or terpolymers, poly(ethersulfones),polycarbonates, liquid crystalline polymers, poly(etheretherketones),and poly(arylates).
 7. The stabilizer of claim 6 wherein thethermoplastic resin is polyethylene or polypropylene.
 8. The stabilizerof claim 1 wherein the stabilizer is of the structure


9. The stabilizer of claim 8 wherein the stabilizer isbis(2,4-di-t-butylphenyl)octylphosphite.
 10. The stabilizer of claim 1wherein the stabilizer is


11. The stabilizer of claim 10 wherein the stabilizer ispoly(4,4′-{2,2′-dimethyl-5,5′-di-t-butylphenylsulfide}octylphosphite).12. A method for stabilizing an organic material comprising adding tosaid organic material a non-xenoestrogenic, phosphorus-containingstabilizer selected from the group consisting of phosphorus-containingcompounds of the structures

wherein y is an integer of from 6 to 20, and

where Z is a linking group, m is 0 or 1, n is an integer of at least 2,the asterisks are independently selected terminal groups, R₁, R₂, R₃,R4, R₅, R6, R₇, and R₈ are independently selected from the groupconsisting of hydrogen, alkyl groups, aralkyl groups, or halogen groupsand Q is selected from the group consisting of

where R₁₁ is alkyl or aralkyl, and


13. The method of claim 12 wherein the organic material is selected fromthe group consisting of rubbers, plastic resins, lubricating oils,petroleum fuels, and waxes.
 14. The method of claim 12 wherein theorganic material is a plastic resin.
 15. The method of claim 14 whereinthe plastic resin is a thermoplastic resin.
 16. The method of claim 15wherein the thermoplastic resin is a thermoplastic polyolefin or anengineering thermoplastic.
 17. The method of claim 15 wherein thethermoplastic resin is selected from the group consisting ofpolyethylene, polypropylene, polystyrenes, polyvinylhalides, polyamides,polyesters, polyphenyleneoxides, polyphenylenesulfides, polyacetals,aliphatic polyketone co or terpolymers, poly(ethersulfones),polycarbonates, liquid crystalline polymers, poly(etheretherketones),and poly(arylates).
 18. The method of claim 17 wherein the thermoplasticresin is polyethylene or polypropylene.
 19. The method of claim 12wherein the stabilizer is of the structure


20. The method of claim 19 wherein the stabilizer isbis(2,4-di-t-butylphenyl)octylphosphite.
 21. The method of claim 12wherein the stabilizer is


22. The method of claim 21 wherein the stabilizer ispoly(4,4′-{2,2′-dimethyl-5,5′-di-t-butylphenylsulfide}octylphosphite).23. A composition of matter comprising an oligomer of the structure

where Z is a linking group, m is 0 or 1, n is an integer of at least 2,the asterisks are independently selected terminal groups, R₁, R₂, R₃,R₄, R₅, R6, R₇, and R₈ are independently selected from the groupconsisting of hydrogen, alkyl groups, aralkyl groups, or halogen groupsand Q is selected from the group consisting of

where R₁₁ is alkyl or aralkyl, and


24. The composition of claim 23 wherein the oligomer ispoly(4,4′-{2,2′-dimethyl-5,5′-di-t-butylphenylsulfide}octylphosphite).